We have our own laboratory for common plastic testing items, and two cooperated labs for regularly authoritative inspection. All extruded plastic profiles are in line with the latest Chinese standard and the European Standard, further more OEM is available.

 

Testing items we can do:

 

Impact Strength

Tensile Strength/Modulus

Elongation at Break

Melting Temp. / DSC

High Temp. Test

 

Low Temp. Test

Flammability (UL94)

Foreign Matter In The Material

Light Transmittance And Haze

Online Defect Detection

Pencil Hardness

Side Light Source Lighting

Surface Structure

Visual Inspection

Weather Resistance

 

For constructional plastic profiles, we do the production and experiment in accordance with the standards below:

• GB/T 23615.1-2017 Accessorial material for architectural aluminum alloy profiles -- Part 1: Thermal barrier strip of polyamide
• EN ISO 527 Tensile properties of plastics
• EN 14024-2004 Metal profiles with thermal barrier -- Mechanical performance Requirement, proof and tests for assessment
• UL94 Standard for Tests for Flammability of Plastic Materials for Parts in Devices and Appliances
• ASTM E84 Standard Test Method for Surface Burning Characteristics of Building Materials
• NFPA 285 Standard Fire Test Method for Evaluation of Fire Propagation Characteristics of Exterior Non-Load-Bearing Wall Assemblies Containing Combustible Components

Due to the great progress and high performance, we were invited as the earliest member of the Chinese National Standard Committee, after years of development, we became the leader of the Chinese National Standard Committee (for revising of GB/T 23615.1-2017). Below's the performance table of PA Building material in Chinese standard:

No.	Characteristic	Size of Thermal Break	GB/T 23615.1-2017	KAXITE Customize
1	Density		(1.30±0.05)g/cm3	1.25~1.45
2	DSC melting peak temperature		≥255℃	≥255℃
3	Stress cracking by shaft nail		No crack at orifice	No crack at orifice
4	Shao hardness HD		80±5	80±10
5	Low temperature notched impact strength(-30℃±2℃)		≥50kJ/m2	≥50kJ/m2
6	Room temperature longitudinal tensile eigenvalue(23℃±2℃)		≥90MPa	≥100MPa
7	Room temperature longitudinal tensile elongation		≥3%	≥3%
8	Room temperature longitudinal tensile modulus of elasticity		≥4500MPa	≥5500MPa
9	Transverse tensile eigenvalue  in room temperature (23℃±2℃)	I type（Width<20mm）	≥90MPa	80~140MPa
10		I type（Width≥20mm）	≥80MPa
11		special shape	≥25MPa
12	Transverse tensile eigenvalue  in high temperature(90℃±2℃)	I type（Width<20mm）	≥55MPa
13		I type（Width≥20mm）	≥45MPa
14		special shape	≥20MPa
15	Transverse tensile eigenvalue  in low temperature(-30℃±2℃)	I type（Width<20mm）	≥90MPa
16		I type（Width≥20mm）	≥80MPa
17		special shape	≥25MPa
18	Transverse tensile eigenvalue (Hydrolytic resistance, boiling for 4h or keep in 23℃ water for 1000h)	I type（Width<20mm）	≥85MPa
19		I type（Width≥20mm）	≥75MPa
20		special shape	≥22MPa
21	Transverse tensile eigenvalue (Thermal aging properties, 140℃ for 1000h)	I type（Width<20mm）	≥60MPa
22		I type（Width≥20mm）	≥55MPa
23		special shape	≥20MPa
24	Typical value of thermal conductivity	Heat flow metering method	0.30W/(m·K)	0.30W/(m·K)
25	Linear coefficient of expansion		2.3×10-5K-1～3.5×10-5K-1	2.3×10-5K-1～3.5×10-5K-1
26	Fiberglass Content		-	0~70%
27	FLAMMABILITY (UL94)		-	V0/5VA

1. Sample water content less than 0.2% by weight.
2 Normal laboratory condition:23℃±2℃ and 50%土10% relative humidity.